“And the guidelines should apply to other cathode materials besides NMC.”Ī paper on this research appeared in Nature Energy.
NMC CATHODE MELTING POINT FREE
“We now have guidelines that battery manufacturers can use to prepare cathode material that is boundary free and works at high voltage,” said Khalil Amine, an Argonne Distinguished Fellow. Oxygen release measurements at APS and the Advanced Light Source at DOE’s Lawrence Berkeley National Laboratory supported this finding. “Our calculations showed how boundaries lead to oxygen release at high voltage and, therefore, performance decline,” Chan said.Įliminating the boundaries prevents oxygen release and thereby improves the cathode safety and stability with cycling. This oxygen loss leads to degradation with cell cycling. According to nanoscientist Maria Chan in CNM, compared to the regions away from them, boundaries are more vulnerable towards the loss of oxygen atoms when the battery is being charged. By contrast, over the same cycle life, the capacity declined by 60% to 88% in NMC cathodes composed of single crystals with many internal boundaries or with coated polycrystals.Ĭalculations at the atomic scale revealed the mechanism behind the capacity decline in the cathode. Testing of small cells with such single-crystal cathodes at very high voltage showed a 25% increase in energy storage per unit volume, with almost no loss of performance over 100 cycles of testing. Importantly, the team developed a method for producing boundary-free single crystals. “But when we use a technique called synchrotron X-ray diffraction microscopy and other techniques at the APS, we find boundaries hiding inside.” “When we look at the surface morphology of these particles, they look like single crystals,” said physicist Wenjun Liu. Scanning and transmission electron microscopies at CNM verified the finding. It turned out that what scientists had believed were single crystals, as evidenced by electron and X-ray microscopy, actually had boundaries inside. (Image by Maria Chan/Argonne National Laboratory.)ĭifferent X-ray analyses were carried out at five APS beamlines ( 11-BM, 20-BM, 2-ID-D, 11-ID-C and 34-ID-E). So, they subjected these cathode materials to extensive analyses at the Advanced Photon Source ( APS) and Center for Nanoscale Materials ( CNM), DOE Office of Science user facilities at Argonne.īoundaries within cathode materials are undesirable because they lead to performance degradation. The problem the team faced was that cathodes made from both coated polycrystals and single crystals still formed cracks with cycling. Electron microscopy of these particles indicated they have no boundaries. This coating surrounds the large spherical particles and smaller ones inside them.Ī different approach to avoid this cracking involves single-crystal particles. To prevent this, Xu and Argonne colleagues had previously developed a protective polymer coating around each particle. As a result, they have what scientists refer to as grain boundaries between particles, which cause cracking upon battery cycling. The large spherical particles are polycrystalline, with differently oriented crystalline regions. One past approach involved microscale spherical particles consisting of numerous much smaller particles. For several decades, battery researchers have been seeking ways to eliminate these cracks. With charge-discharge cycling, performance rapidly declines due to cracks forming in the cathode particles. “The present-day NMC cathode has posed a major barrier to operation at high voltage,” said Guiliang Xu, assistant chemist. “We now have guidelines that battery manufacturers can use to prepare cathode material that is boundary free and works at high voltage.” - Khalil Amine, Argonne Distinguished Fellow The team’s new structure for the cathode’s micro-sized particles could lead to longer-lasting and safer batteries able to operate at very high voltage and power vehicles for longer driving ranges. Batteries with this cathode now power the Chevy Bolt.Īrgonne researchers have made another breakthrough with the NMC cathode. Many of these discoveries have focused on a battery cathode known as NMC, a nickel-manganese-cobalt oxide. Department of Energy’s ( DOE) Argonne National Laboratory have a long history of breakthrough discoveries with lithium-ion batteries.
0 kommentar(er)
